Fender Pads

Brand:

QIYUAN

Product Origin:

Dezhou, China

Delivery time:

15-25 days

Supply Capacity:

8000 Tons/Yea

Key words:

Product description

UHMWPE is a unique, low friction Ultra High Molecular Weight Polyethylene (UHMWPE) with a molecular weight of more than 3 million. Combining the benefits of higher wear resistance (even greater than steel) and lower maintenance costs, the pads are easy to fabricate, install and can be fastened to steel, concrete, wood and rubber.

◇ Light weight
◇ Superior high impact strength
◇ High abrasion resistance
◇ Low co-efficient of friction
◇ Shock and noise absorption
◇ Excellent self-lubrication
◇ Good chemical resistance
◇ Excellent UV stability
◇ Ozone resistant
◇ 100% recyclable
◇ Non toxic
◇ Temperature resistant (-100℃ to +80 ℃)
◇ No moisture absorption
◇ Can be supplied pre-drilled for easy installation and chamfered to avoid snagging

Property

Test Method

Virgin Material

Unit

Molecular weight

 

3~9 million

g/mol

Density

ISO 1183-1:2012 /DIN53479

0.92-0.98

g/cm3

Compression Strength

ISO 604:2002

≥32

Mpa

Tensile Strength

ISO527-2:2012

≥22

Mpa

Elongation at break

ISO527-2:2012

≥280

%

Dynamic Friction coefficient

ASTM D 1894 /GB10006-88

≤0.18

 

Notched impact strength(Charpy)

ISO179-1:2010/GB/T 1043.1-2008

≥100

kJ/m2

Vicat softing point

ISO306:2004

≥80

Hardness Shore-D

ISO 868:2003

61-66

D

Values are averages and are not specifications. ASTM test methods are under current procedures.

The manufacturing process does not limit the cross-sections and plate dimensions:

◇ Thickness from 6-300mm
◇ Plates size 1000 ×1000mm up to 6000 ×2000mm

The standard color is black. Other colors such as blue, green, yellow, white or red is available upon request. 

Your message is welcome to consult.

The company adopts international advanced production procedures, introduces advanced testing equipment, and implements strict inspection of raw material supply.